ASTM A203/A203M nickel alloy steel plates are widely used in the manufacture of pressure vessels and low-temperature equipment.2026-05-09
-
ASTM A202 Grade B is a chromium-manganese-silicon low-alloy steel tailored for high-pressure, medium-temperature pressure vessel applications.2026-04-30
-
ASTM A202 Grade A is a critical chromium-manganese-silicon low-alloy steel plate specifically designed for welded pressure vessels and boilers operating at medium temperatures.2026-04-30
-
ASTM A202 Pressure Vessel Steel Material and Grades:
Alloy System: **Chromium-Manganese-Silicon (Cr-Mn-Si)** Low-Alloy Heat-Resistant Steel2026-04-17 -
ASTM A204/A204M Grade B molybdenum alloy steel plates for pressure vessels feature superior chemical composition and mechanical properties compared to Grade A2026-04-10
Need advice, or a quote?
A517 grade A steel plate,A517 grade A steel chemical composition
A517 grade A steel plate is a kind of high tensile alloy steel, it is mainly used in fusion welded boilers and other pressure vessels. More information about A517 grade A steel plate technology, please see the following:
A517 grade A steel plate specification:
Grade: A517 grade A Standard: ASTM A517/A517M
Thickness:3mm -260mm, Width :1000mm-4000mm, Length :1000mm-18000mm
A517 grade A steel chemical composition:
|
C % |
Mn % |
P % |
S % |
SI % |
Ni % |
Cr % |
|
0.13-0.23 |
0.74-1.20 |
0.035 |
0.035 |
0.34-0.86 |
|
0.46-0.84 |
|
Mo % |
B % |
V % |
Ti % |
Zr % |
Cu % |
Co % |
|
0.15-0.31 |
0.025 |
|
|
0.04-0.16 |
|
|
|
Grade |
||||
|
Thickness |
Yield |
Tensile |
Elongation |
|
|
A517 grade A |
mm |
Min Mpa |
Mpa |
Min % |
|
6-65 |
690 |
795-930 |
16% |
|
|
65-150 |
620 |
725-930 |
14% |
|
A517 grade A steel plate application:
A517 grade A steel plate is widely used in pressure vessel, boiler, storage tanks and heat exchanger in oil, gas project.
A517 grade A steel plate additional condition :
UT (Ultrasonic examination), AR(As Hot Rolled only), TMCP(Thermal Mechanical Control Processing),N(Normalized), Q+T(Quenched and Tempered), Z Direction Test(Z15, Z25, Z35), Charpy V-Notch Impact Test, HIC test, NDT, PWHT( Simulated Post Weld Heat Treatment), NACE0175, The Third Party Test (Such as SGS Test), Coated or Shot Blasting and Painting.
Any need in A517 grade A steel plate, please feel free to contact us, we will reply you as soon as possible.