DIN17102 E St E 315 steel is a German standard low-alloy high-strength steel plate widely used in multiple industrial fields. Below is a detailed introduction to its production process and application scope2024-11-01
-
Hot rolled ASTM A516 Grade 70 high strength boiler steel plate is a specialized type of steel plate designed for use in pressure vessel and boiler applications.2024-03-15
-
ASTM A515, A516, and A537 are commonly used specifications for hot rolled carbon steel plates in various industrial applications, especially in pressure vessel2024-03-07
-
15Mo3 and 16Mo3 are high-strength boiler steel plates used in the construction of pressure vessels operating at elevated temperatures and pressures. These grade2024-03-07
-
ASTM A387 Grade 22 Class 1 and Class 2 alloy steel pressure vessel plates are high-quality materials designed for elevated temperature service in pressure vesse2024-02-20
KS D3562 SPPS38 carbon steel pipe application
SPPS38 carbon steel pipe supplier, SPPS38 carbon steel pipe exporter, SPPS38 carbon steel pipe manufacturer in China.
Application of SPPS38 carbon steel pipe: structure, electric power transmission tower projects, piling, water, oil & gas pipeline engineering, mechanical industry, municipal projects, roads and its auxiliary facilities, etc.
Size range of SPPS38 carbon steel pipe:
|
Outer diameter |
ERW / HFW |
LSAW / DSAW |
SSAW / HSAW |
RHS |
SHS |
|
1/8 - 20 inch |
12 - 56 inch |
8 - 126 inch |
40 x 20 mm - |
15 x 15 mm - |
|
|
Wall thickness |
0.4 - 16 mm |
6.0 - 40 mm |
6.0 - 26 mm |
1.0 - 30 mm |
0.6 - 30 mm |
|
Length |
5.8 ~ 12.0 m or upon customers' requirements |
||||
Chemical composition of SPPS38 carbon steel pipe (% , Max)
C : 0.25
Si : 0.35
Mn : 0.30~0.90
P : 0.040
S : 0.040
Mechanical properties of SPPS38 carbon steel pipe (N/㎟, Min)
Yield point or Yield strength (YS) : 220
Tensile strength(TS) : 380
More information about the SPPS38 carbon steel pipe, such as SPPS38 carbon steel pipe price, SPPS38 carbon steel pipe delivery type, you can contact us at any times.