The demand for reliable materials in cryogenic service applications has increased significantly with the rapid growth of LNG terminals, industrial gas storage facilities, and low-temperature pressure vessels.2026-06-24
-
As the global demand for liquefied natural gas (LNG) continues to grow, the need for reliable materials for cryogenic storage systems has become increasingly important.2026-06-18
-
For engineers specifying materials for cryogenic pressure vessels, finding the balance between strength and ductility at sub-zero temperatures is challenging.2026-06-12
-
In industries where equipment must operate reliably under freezing or cryogenic conditions, material selection becomes a matter of safety and structural integrity.2026-06-01
-
While both ASTM A203 Grade B and ASTM A106 Grade B serve critical roles in industrial applications, they are fundamentally different in composition, purpose, and performance.2026-06-01
EN 10028-3 P275NH steel,P275NH steel Tensile Requirements
EN 10028-3 P275NH steel is a kind steel for pressure purposes (P) with minimum yield strength of 275 MPa (275) which has specified elevated temperature properties (NH).
EN 10028-3 P275NH steel Chemical Requirements:
|
C |
Si |
Mn |
P |
S |
Altotal |
N |
Cr |
|
0.16 |
0.40 |
0.80-1.50 |
0.025 |
0.015 |
0.020 min |
0.012 |
0.30 |
|
Cu |
Mo |
Nb |
Ni |
Ti |
V |
Nb+Ti+V |
|
|
0.30 |
0.08 |
0.05 |
0.50 |
0.03 |
0.05 |
0.05 |
|
EN 10028-3 P275NH steel Tensile Requirements:
|
Product Thickness |
Yield Strength MPa |
Tensile Strength MPa |
Elongation A% |
|
up to 16 mm |
275 min |
390 to 510 |
24 min |
|
16 to 40 mm |
265 min |
390 to 510 |
24 min |
|
over 40 to 60 mm |
255 min |
390 to 510 |
24 min |
|
over 60 to 100 mm |
235 min |
370 to 490 |
23 min |
|
over 100 to 150 mm |
225 min |
360 to 480 |
23 min |
|
over 150 to 250 mm |
215 min |
350 to 470 |
23 min |
EN 10028-3 P275NH steel Impact energy values for the normalised condition:
|
|
-20 oC |
0 oC |
+20 oC |
|
Transverse |
30 J min |
40 J min |
50 J min |
|
Longitudinal |
45 J min |
65 J min |
75 J min |
EN 10028-3 P275NH steel Min. values for proof strength Rp0,2 (MPa) at elevated temperatures:
|
Thickness |
50oC |
100oC |
150oC |
200oC |
250oC |
300oC |
350oC |
400oC |
|
up to 16 mm |
266 |
250 |
232 |
213 |
195 |
179 |
166 |
156 |
|
16 to 40 mm |
256 |
241 |
223 |
205 |
188 |
173 |
160 |
150 |
|
over 40 to 60 mm |
247 |
232 |
215 |
197 |
181 |
166 |
154 |
145 |
|
over 60 to 100 mm |
227 |
214 |
198 |
182 |
167 |
153 |
142 |
133 |
|
over 100 to 150 mm |
218 |
205 |
190 |
174 |
160 |
147 |
136 |
128 |
|
over 150 to 250 mm |
208 |
196 |
181 |
167 |
153 |
140 |
130 |
122 |
More informations about EN 10028-3 P275NH steel, please contact us--BEBON STEEL.