The demand for reliable materials in cryogenic service applications has increased significantly with the rapid growth of LNG terminals, industrial gas storage facilities, and low-temperature pressure vessels.2026-06-24
-
As the global demand for liquefied natural gas (LNG) continues to grow, the need for reliable materials for cryogenic storage systems has become increasingly important.2026-06-18
-
For engineers specifying materials for cryogenic pressure vessels, finding the balance between strength and ductility at sub-zero temperatures is challenging.2026-06-12
-
In industries where equipment must operate reliably under freezing or cryogenic conditions, material selection becomes a matter of safety and structural integrity.2026-06-01
-
While both ASTM A203 Grade B and ASTM A106 Grade B serve critical roles in industrial applications, they are fundamentally different in composition, purpose, and performance.2026-06-01
EN 10028-3 P355NH steel,P355NH steel Tensile Requirements
EN 10028-3 P355NH steel is steel for pressure purposes (P) with minimum yield strength of 355 MPa (355) which has specified elevated temperature properties (NH).
EN 10028-3 P355NH steel Chemical Requirements:
|
C |
Si |
Mn |
P |
S |
Altotal |
N |
Cr |
|
0.18 |
0.50 |
1.10-1.70 |
0.025 |
0.015 |
0.020 min |
0.012 |
0.30 |
|
Cu |
Mo |
Nb |
Ni |
Ti |
V |
Nb+Ti+V |
|
|
0.30 |
0.08 |
0.05 |
0.50 |
0.03 |
0.10 |
0.12 |
|
EN 10028-3 P355NH steel Tensile Requirements:
|
Product Thickness |
Yield Strength MPa |
Tensile Strength MPa |
Elongation A% |
|
up to 16 mm |
355 min |
490 to 630 |
22 min |
|
16 to 40 mm |
345 min |
490 to 630 |
22 min |
|
over 40 to 60 mm |
335 min |
490 to 630 |
22 min |
|
over 60 to 100 mm |
315 min |
470 to 610 |
21 min |
|
over 100 to 150 mm |
305 min |
460 to 600 |
21 min |
|
over 150 to 250 mm |
295 min |
450 to 590 |
21 min |
EN 10028-3 P355NH steel Impact energy values for the normalised condition:
|
|
-20 oC |
0 oC |
+20 oC |
|
Transverse |
30 J min |
40 J min |
50 J min |
|
Longitudinal |
45 J min |
65 J min |
75 J min |
EN 10028-3 P355NH steel Min. values for proof strength Rp0,2 (MPa) at elevated temperatures:
|
Thickness |
50oC |
100oC |
150oC |
200oC |
250oC |
300oC |
350oC |
400oC |
|
up to 16 mm |
343 |
323 |
299 |
275 |
252 |
232 |
214 |
202 |
|
16 to 40 mm |
334 |
314 |
291 |
267 |
245 |
225 |
208 |
196 |
|
over 40 to 60 mm |
324 |
305 |
282 |
259 |
238 |
219 |
202 |
190 |
|
over 60 to 100 mm |
305 |
287 |
265 |
244 |
224 |
206 |
190 |
179 |
|
over 100 to 150 mm |
295 |
277 |
257 |
236 |
216 |
199 |
184 |
173 |
|
over 150 to 250 mm |
285 |
268 |
249 |
228 |
209 |
192 |
178 |
167 |
More informations about EN 10028-3 P355NH steel, please contact us--BEBON STEEL.