The demand for reliable materials in cryogenic service applications has increased significantly with the rapid growth of LNG terminals, industrial gas storage facilities, and low-temperature pressure vessels.2026-06-24
-
As the global demand for liquefied natural gas (LNG) continues to grow, the need for reliable materials for cryogenic storage systems has become increasingly important.2026-06-18
-
For engineers specifying materials for cryogenic pressure vessels, finding the balance between strength and ductility at sub-zero temperatures is challenging.2026-06-12
-
In industries where equipment must operate reliably under freezing or cryogenic conditions, material selection becomes a matter of safety and structural integrity.2026-06-01
-
While both ASTM A203 Grade B and ASTM A106 Grade B serve critical roles in industrial applications, they are fundamentally different in composition, purpose, and performance.2026-06-01
DIN17165 19 Mn 8 steel
DIN17165 19 Mn 8 steel is a boiler and pressure vessel steel grade.
DIN17165 19 Mn 8 steel is mainly used to for manufacturing boilers, pressure vessels and pipes transporting hot liquids.
DIN17165 19 Mn 8 steel Chemical Composition:
Carbon (C) 0.10-0.22
Manganese (Mn) 1.10-1.70
Silicon (Si) ≤0.60
Phosphorous (P) ≤0.025
Sulphur (S) ≤0.015
Aluminium (Al) ≤0.020
Nitrogen (N) ≤0.012
Chromium (Cr) ≤0.30
Copper (Cu) ≤0.30
Molybdenum (Mo) ≤0.08
Niobium (Nb) ≤0.020
Nickel (Ni) ≤0.30
Titanium (Ti) ≤0.03
Vanadium (Vi) ≤0.02
DIN17165 19 Mn 8 steel Specification:
Thickness:6mm-300mm
Width:1500mm-4050mm
Length:3000mm-15000mm
About DIN17165 19 Mn 8 steel Mechanical Property, different thickness has different property, such as:
When thickness is below 16mm, Min Yield is 355 Mpa, Tensilmie is 510-650 Mpa.
When thickness is between 16mm to 40mm, Min Yield is 345 Mpa, Tensilmie is 510-650 Mpa.
When thickness is between 40mm to 60mm, Min Yield is 335 Mpa, Tensilmie is 510-650 Mpa.
When thickness is between 60mm to 100mm, Min Yield is 315 Mpa, Tensilmie is 490-630 Mpa.
When thickness is between 100mm to 150mm, Min Yield is 295 Mpa, Tensilmie is 480-630 Mpa.
When thickness is between 150mm to 250mm, Min Yield is 280 Mpa, Tensilmie is 470-630 Mpa.
However, there are also differences between each other. The same is that, the Min Elongation is 20%, the Min Impact Energy at -20°is 27 KV J, at 0°is 34 KV J, at 20°is 40 KV J.